Physical Properties List

Copy and paste this link to your website, so they can see this document directly without any plugins.



Keywords

23℃50%RH, 0.75mmt, 1.41, 600250, 1.6~2.0, 1.42, 1.8~2.2, 1.5mmt, Asahi, Kasei, Dielectric, High, Tensile, Strength, 2700, Viscosity, 100HZ, scale), Rockwell, KJ/m2, 2039, Tangent, Temperature, Right-angle), Deflection, Under, Load, 60093, Resistivity, UL-94

Transcript

TENACTM
HighDurability
High
Viscosity
HighDurability
Medium
Viscosity
Medium Viscosity
ImpactResistant
Soft
Medium
Viscosity
High-Cycle
High
Flowability
High Flowability
High-Cycle
Super High
Flowability
Test
method
Units Condition 2010 3010 MG210 4050 4010 4060 5010 4012 5050 7010 7050 7054 9054
Density ISO 1183 g/cm3 1.42 1.42 1.42 1.42 1.42 1.42 1.42 1.42 1.42 1.42 1.42 1.42 1.42
Moisture Regain ISO 62 %
Yield Stress ISO 527 MPa 23℃50%RH 70 70 75 76 71 70 72 66 73 73 73 74 74
Tensile Strain at Yield ISO 527 % 23℃50%RH
Tensile Stress at Break ISO 527 MPa 23℃50%RH
Tensile Strain at Break ISO 527 % 23℃50%RH 55 50 40 30 40 40 30 40 25 20 20 15 12
Tensil Modulus ISO 527 MPa 23℃50%RH 2900 3000 3150 3300 3200 3000 3300 2700 3300 3400 3400 3400 3500
Flexural strenght ISO 178 MPa 23℃50%RH
Flexural Modulus ISO 178 MPa 23℃50%RH 2700 2800 2900 3000 2900 2900 3100 2500 3100 3200 3200 3200 3300
Notched Charpy Impact Strength ISO 179 KJ/m2 15 13 10 11 10 9 8 10 7 7 6 6 4
Charpy Impact Strength ISO 179 KJ/m2
Rockwell Hardness(R scale) ISO 2039
Rockwell Hardness(M scale) ISO 2039
Linear Expansion Coefficient ISO 11359 ×10
-5
㎜/㎜/℃ 10 10 10 10 10 10 10 10 10 10 10 10 10
Deflection Temperature Under Load
(1.82MPa)
ISO 75 ℃ 100 100 103 110 105 100 105 80 105 105 105 105 105
Deflection Temperature Under Load
(0.45MPa)
ISO 75 ℃ 163 163 167 165 165 163 165 151 165 165 165 165 165
UL-94(1/16 in) UL-94 Rank 1.6mm 1.5mmt HB 1.5mmt HB - - 1.5mmt HB - 1.5mmt HB 1.5mmt HB 1.5mmt HB 1.5mmt HB 1.5mmt HB 1.5mmt HB UL-94(1/32 in) UL-94 Rank 0.8mm 0.8mmt HB - - 0.75mmt - 0.75mmt - 0.84mmt 0.81mmt 0.71mmt 0.75mmt 0.75mmt 0.75mmt
UL94-5VA UL94-5VA mm - - - - - - - - - - - - -
Tracking Resistance IEC 60112 3mm - - - - - - - - - - - - Dielectric Strength IEC 60243 KV/㎜ - - - - - - - - - - - - Surface Resistivity IEC 60093 Ω 23℃50%RH - - - - - - - - - - - - Volume Resistivity IEC 60093 Ω・㎝ 23℃50%RH - - - - - - - - - - - - Dielectric Loss Tangent IEC 600250 100HZ - - - - - - - - - - - - Dielectric Loss Tangent IEC 600250 1MHZ - - - - - - - - - - - - Permittivity IEC 600250 100HZ - - - - - - - - - - - - Permittivity IEC 600250 1MHZ - - - - - - - - - - - - Asahi Kasei % 1.8~2.2 1.8~2.2 1.7~2.1 1.8~2.2 1.8~2.2 1.8~2.2 1.8~2.2 1.8~2.2 1.7~2.1 1.8~2.2 1.7~2.1 1.7~2.1 1.7~2.1
ISO 294-4 %
Refractive Index ISO 489
Transmission ISO13468-1
Melt Flow Rate ISO 1133 g/10min 1.7 2.8 1.7 7 10 17 22 10 21 34 34 39 70
Mold shrinkage (Flow / Right-angle)
P
h ys ic a ls The date provided for these properties are typical values,intended only as guides,and should not be construed as sales specifications.
For any intended use that may involve food contact,therefore,please consult with Asahi Kasei Chemicals Corporation.
For safety in the handling and use of TenacTM,TenacTM-C,please refer to the relevant Material Safety Data Sheet issued by Asahi Kasei Chemicals Corporation.
High Viscosity
M
e c h an ic al T
h e rm al F
la m m ab ili
ty E
le c tr ic al s Mold shrinkage (Flow / Right-angle)
High
Viscosity
Medium Viscosity High Flowability
High
Flowability
High-Cycle
HighLubricity soft
Test
method
Units Condition 3510 4520 5520 7520 8520 7554 HC350 HC450 HC550 HC750 HC460 HC760 SG454
Density ISO 1183 g/cm3 1.41 1.41 1.41 1.41 1.41 1.41 1.41 1.41 1.41 1.41 1.41 1.41 1.10
Moisture Regain ISO 62 %
Yield Stress ISO 527 MPa 23℃50%RH 62 63 63 64 65 66 66 67 67 68 66 67 32
Tensile Strain at Yield ISO 527 % 23℃50%RH
Tensile Stress at Break ISO 527 MPa 23℃50%RH
Tensile Strain at Break ISO 527 % 23℃50%RH 40 35 33 30 25 25 40 35 33 30 40 30 80
Tensil Modulus ISO 527 MPa 23℃50%RH 2500 2700 2700 2800 2850 2900 2650 2800 2850 3000 2750 2900 1300
Flexural strenght ISO 178 MPa 23℃50%RH
Flexural Modulus ISO 178 MPa 23℃50%RH 2400 2500 2500 2600 2700 2700 2550 2650 2700 2800 2600 2750 1300
Notched Charpy Impact Strength ISO 179 KJ/m2 9 7 6 5 4.5 4 9 7 6 5 7 6 5
Charpy Impact Strength ISO 179 KJ/m2
Rockwell Hardness(R scale) ISO 2039
Rockwell Hardness(M scale) ISO 2039
Linear Expansion Coefficient ISO 11359 ×10
-5
㎜/㎜/℃ 10 10 10 10 10 10 10 10 10 10 10 10 10
Deflection Temperature Under Load
(1.82MPa)
ISO 75 ℃ 95 100 100 100 100 100 102 105 105 105 102 103 74
Deflection Temperature Under Load
(0.45MPa)
ISO 75 ℃ 156 156 156 157 156 157 160 160 160 161 158 159 152
UL-94(1/16 in) UL-94 Rank 1.6mm 1.5mmt HB 1.5mmt HB 1.5mmt HB 1.5mmt HB - - - - - - - - UL-94(1/32 in) UL-94 Rank 0.8mm
0.81mmt
HB
0.75mmt
HB
0.75mmt
HB
0.75mmt
HB
0.75mmt
HB
0.75mmt
HB
0.75mmt
HB
0.80mmt
HB
0.75mmt
HB
0.75mmt
HB
0.75mmt
HB
0.75mmt
HB
1.0mmt HB
UL94-5VA UL94-5VA mm - - - - - - - - - - - - -
Tracking Resistance IEC 60112 3mm - - - - - - - - - - - - Dielectric Strength IEC 60243 KV/㎜ - - - - - - - - - - - - Surface Resistivity IEC 60093 Ω 23℃50%RH - - - - - - - - - - - - Volume Resistivity IEC 60093 Ω・㎝ 23℃50%RH - - - - - - - - - - - - Dielectric Loss Tangent IEC 600250 100HZ - - - - - - - - - - - - Dielectric Loss Tangent IEC 600250 1MHZ - - - - - - - - - - - - Permittivity IEC 600250 100HZ - - - - - - - - - - - - Permittivity IEC 600250 1MHZ - - - - - - - - - - - - Asahi Kasei % 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0
ISO 294-4 %
Refractive Index ISO 489
Transmission ISO13468-1
Melt Flow Rate ISO 1133 g/10min 2.8 9 15 30 45 30 2.8 8 15 30 8 30 5
F
la m m a b ili
ty E
le c tr ic al s Mold shrinkage (Flow / Right-angle)
Mold shrinkage (Flow / Right-angle)
P
h ys ic a ls The date provided for these properties are typical values,intended only as guides,and should not be construed as sales specifications.
For any intended use that may involve food contact,therefore,please consult with Asahi Kasei Chemicals Corporation.
For safety in the handling and use of TenacTM,TenacTM-C,please refer to the relevant Material Safety Data Sheet issued by Asahi Kasei Chemicals Corporation.
TENACTM-C
HC Series
Low abrasional
attacking
M
e c h an ic al T
h e rm al TENACTM TENACTM -C
High
Viscosity
Medium
Viscosity
Standard grades HC Series
HighLuricity
Low
abrasional
attacking
High Flowability
High Stiffiness
Test
method
Units Condition Z3010 Z4060 Z3510 Z4520 ZH450 Z4513 Z4563 ZLV40 ZH760 ZLD75
Density ISO 1183 g/cm3 1.42 1.42 1.41 1.41 1.41 1.41 1.41 1.41 1.41 1.52
Moisture Regain ISO 62 %
Yield Stress ISO 527 MPa 23℃50%RH 70 70 62 63 67 63 61 61 67 53
Tensile Strain at Yield ISO 527 % 23℃50%RH
Tensile Stress at Break ISO 527 MPa 23℃50%RH
Tensile Strain at Break ISO 527 % 23℃50%RH 50 40 40 35 35 35 35 20 30 10
Tensil Modulus ISO 527 MPa 23℃50%RH 3000 3000 2500 2700 2800 2550 2500 2700 2900 3500
Flexural strenght ISO 178 MPa 23℃50%RH
Flexural Modulus ISO 178 MPa 23℃50%RH 2800 2900 2400 2500 2650 2450 2350 2600 2750 3400
Notched Charpy Impact Strength ISO 179 KJ/m2 13 9 9 7 7 7 6 5 6 3
Charpy Impact Strength ISO 179 KJ/m2
Rockwell Hardness(R scale) ISO 2039
Rockwell Hardness(M scale) ISO 2039
Linear Expansion Coefficient ISO 11359 ×10
-5
㎜/㎜/℃ 10 10 10 10 10 10 10 10 10 8
Deflection Temperature Under
Load (1.82MPa)
ISO 75 ℃ 100 100 95 100 106 97 91 100 103 110
Deflection Temperature Under
Load (0.45MPa)
ISO 75 ℃ 163 163 156 156 160 154 152 157 159 160
UL-94(1/16 in) UL-94 Rank 1.6mm - - - - - UL-94(1/32 in) UL-94 Rank 0.8mm
0.75mmt
HB
- -
0.79mmt
HB
0.75mmt
HB
0.75mmt HB
UL94-5VA UL94-5VA mm - - - - - - - -
Tracking Resistance IEC 60112 3mm - - - - - - - Dielectric Strength IEC 60243 KV/㎜ - - - - - - - Surface Resistivity IEC 60093 Ω 23℃50%RH - - - - - - - Volume Resistivity IEC 60093 Ω・㎝ 23℃50%RH - - - - - - - Dielectric Loss Tangent IEC 600250 100HZ - - - - - - - Dielectric Loss Tangent IEC 600250 1MHZ - - - - - - - Permittivity IEC 600250 100HZ - - - - - - - Permittivity IEC 600250 1MHZ - - - - - - - Asahi Kasei % 1.8~2.2 1.8~2.2 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0 1.4~1.6
ISO 294-4 %
Refractive Index ISO 489
Transmission ISO13468-1
Melt Flow Rate ISO 1133 g/10min 2.4 17 2.8 9 8 9 9 9 30 25
Mold shrinkage (Flow / Right-angle)
P
h ys ic a ls The date provided for these properties are typical values,intended only as guides,and should not be construed as sales specifications.
For any intended use that may involve food contact,therefore,please consult with Asahi Kasei Chemicals Corporation.
For safety in the handling and use of TenacTM,TenacTM-C,please refer to the relevant Material Safety Data Sheet issued by Asahi Kasei Chemicals Corporation.
Weather-resistant
M
e c h an ic al T
h e rm al F
la m m a b ili
ty E
le ct ri ca ls Mold shrinkage (Flow / Right-angle)
TENACTM -C Weather-resistant
Medium Viscosity High Viscosity Medium Viscosity
High
Flowability
Test
method
Units Condition 2013A 3013A 4013A 5013A 3513 4513 4563 7513
Density ISO 1183 g/cm3 1.42 1.42 1.42 1.42 1.41 1.41 1.41 1.41
Moisture Regain ISO 62 %
Yield Stress ISO 527 MPa 23℃50%RH 68 69 70 71 62 63 61 64
Tensile Strain at Yield ISO 527 % 23℃50%RH
Tensile Stress at Break ISO 527 MPa 23℃50%RH
Tensile Strain at Break ISO 527 % 23℃50%RH 50 45 40 30 40 35 35 30
Tensil Modulus ISO 527 MPa 23℃50%RH 2800 2900 3000 3100 2500 2550 2500 2750
Flexural strenght ISO 178 MPa 23℃50%RH
Flexural Modulus ISO 178 MPa 23℃50%RH 2500 2600 2700 2900 2400 2450 2350 2600
Notched Charpy Impact Strength ISO 179 KJ/m2 15 13 10 8 8 7 6 5
Charpy Impact Strength ISO 179 KJ/m2
Rockwell Hardness(R scale) ISO 2039
Rockwell Hardness(M scale) ISO 2039
Linear Expansion Coefficient ISO 11359 ×10-5㎜/㎜/℃ 10 10 10 10 10 10 10 10
Deflection Temperature Under Load
(1.82MPa)
ISO 75 ℃ 97 97 102 102 93 97 91 100
Deflection Temperature Under Load
(0.45MPa)
ISO 75 ℃ 163 163 164 164 153 154 152 156
UL-94(1/16 in) UL-94 Rank 1.6mm - - - - - - - UL-94(1/32 in) UL-94 Rank 0.8mm - - - - - - - UL94-5VA UL94-5VA mm - - - - - - - -
Tracking Resistance IEC 60112 3mm - - - - - - - Dielectric Strength IEC 60243 KV/㎜ - - - - - - - Surface Resistivity IEC 60093 Ω 23℃50%RH - - - - - - - Volume Resistivity IEC 60093 Ω・㎝ 23℃50%RH - - - - - - - Dielectric Loss Tangent IEC 600250 100HZ - - - - - - - Dielectric Loss Tangent IEC 600250 1MHZ - - - - - - - Permittivity IEC 600250 100HZ - - - - - - - Permittivity IEC 600250 1MHZ - - - - - - - Asahi Kasei % 1.8~2.2 1.8~2.2 1.8~2.2 1.8~2.2 1.6~2.0 1.6~2.0 1.6~2.0 1.6~2.0
ISO 294-4 %
Refractive Index ISO 489
Transmission ISO13468-1
Melt Flow Rate ISO 1133 g/10min 1.7 2.8 10 22 3 9 9 30
Mold shrinkage (Flow / Right-angle)
Mold shrinkage (Flow / Right-angle)
P
h ys ic a ls The date provided for these properties are typical values,intended only as guides,and should not be construed as sales specifications.
For any intended use that may involve food contact,therefore,please consult with Asahi Kasei Chemicals Corporation.
For safety in the handling and use of TenacTM,TenacTM-C,please refer to the relevant Material Safety Data Sheet issued by Asahi Kasei Chemicals Corporation.
TENACTM Weather-resistant
High Viscosity
M
e c h an ic al T
h e rm al F
la m m a bi lit
y E
le c tr ic al s TENACTM TENACTM -C
Glass-Reinforced Glass-Reinforced
Mineral
Reinforced
Carvon-Fiber Reinforced
Test
method
Units Condition GA510 GA520 GN705 GN455 GN755 MT754 CF452 CF454
Density ISO 1183 g/cm3 1.50 1.56 1.59 1.59 1.59 1.58 1.43 1.46
Moisture Regain ISO 62 %
Yield Stress ISO 527 MPa 23℃50%RH 62 54
Tensile Strain at Yield ISO 527 % 23℃50%RH
Tensile Stress at Break ISO 527 MPa 23℃50%RH 110 120 120 61 110 130
Tensile Strain at Break ISO 527 % 23℃50%RH 15 10 2 2 2 5 2 1
Tensil Modulus ISO 527 MPa 23℃50%RH 3400 4300 9000 8000 8000 4800 7500 13000
Flexural strenght ISO 178 MPa 23℃50%RH
Flexural Modulus ISO 178 MPa 23℃50%RH 3200 4100 8500 7500 7500 4800 7000 12500
Notched Charpy Impact Strength ISO 179 KJ/m2 4 4 7 7 7 3 4 5
Charpy Impact Strength ISO 179 KJ/m2
Rockwell Hardness(R scale) ISO 2039
Rockwell Hardness(M scale) ISO 2039
Linear Expansion Coefficient ISO 11359 ×10-5㎜/㎜/℃ 8 7 4~9 4~9 4~9 6 6~9 4~9
Deflection Temperature Under Load
(1.82MPa)
ISO 75 ℃ 110 118 171 163 163 131 161 163
Deflection Temperature Under Load
(0.45MPa)
ISO 75 ℃ 165 165 175 165 165 161 165 166
UL-94(1/16 in) UL-94 Rank 1.6mm - 1.5mmt HB - 1.5mmt HB 1.5mmt HB 1.5mmt HB - UL-94(1/32 in) UL-94 Rank 0.8mm
0.73mmt
HB
0.71mmt
HB
0.75mmt
HB
0.75mmt
HB
0.75mmt
HB
0.75mmt
HB
0.75mmt
HB
0.75mmt
HB
UL94-5VA UL94-5VA mm - - - - - - - -
Tracking Resistance IEC 60112 3mm - - - - - - - Dielectric Strength IEC 60243 KV/㎜ - - - - - - - Surface Resistivity IEC 60093 Ω 23℃50%RH - - - - - - - Volume Resistivity IEC 60093 Ω・㎝ 23℃50%RH - - - - - - - Dielectric Loss Tangent IEC 600250 100HZ - - - - - - - Dielectric Loss Tangent IEC 600250 1MHZ - - - - - - - Permittivity IEC 600250 100HZ - - - - - - - Permittivity IEC 600250 1MHZ - - - - - - - Asahi Kasei %
1.5~1.8
/ 1.0~1.3
1.5~1.8
/1.0~1.3
0.4~0.6
/1.0~1.2
0.4~0.6
/1.0~1.2
0.4~0.6
/1.0~1.2
1.0~1.2
0.3~0.6
/0.8~1.2
0.1~0.2
/0.6~0.8
ISO 294-4 %
Refractive Index ISO 489
Transmission ISO13468-1
Melt Flow Rate ISO 1133 g/10min 17 15 10 4 8 20 5 4P
h ys ic a ls The date provided for these properties are typical values,intended only as guides,and should not be construed as sales specifications.
For any intended use that may involve food contact,therefore,please consult with Asahi Kasei Chemicals Corporation.
For safety in the handling and use of TenacTM,TenacTM-C,please refer to the relevant Material Safety Data Sheet issued by Asahi Kasei Chemicals Corporation.
M
e c h an ic al T
h e rm al F
la m m a bi lit
y E
le c tr ic al s Mold shrinkage (Flow / Right-angle)
Mold shrinkage (Flow / Right-angle)
TENAC
TM
High-Luricity TENAC
TM
-C High-Luricity
High
Flowability
High Viscosity
High
Viscosity
High
Viscosity
Medium
Viscosity
High
Flowability
High Flowability
High Stiffiness
Test
method
Units Condition LS701 LT804 LT805 LT200 FS410 LA543 LM511 LT802 LT350 LV450 LZ750 LD755
Density ISO 1183 g/cm3 1.42 1.42 1.42 1.40 1.46 1.38 1.42 1.42 1.41 1.41 1.39 1.52
Moisture Regain ISO 62 %
Yield Stress ISO 527 MPa 23℃50%RH 65 68 69 61 65 63 65 68 58 61 62 53
Tensile Strain at Yield ISO 527 % 23℃50%RH
Tensile Stress at Break ISO 527 MPa 23℃50%RH
Tensile Strain at Break ISO 527 % 23℃50%RH 20 45 40 35 18 30 25 50 45 20 15 10
Tensil Modulus ISO 527 MPa 23℃50%RH 3100 2900 3100 2700 3100 2800 3000 2700 2500 2700 2700 3500
Flexural strenght ISO 178 MPa 23℃50%RH
Flexural Modulus ISO 178 MPa 23℃50%RH 2700 2700 2800 2600 3000 2600 2800 2600 2300 2600 2700 3400
Notched Charpy Impact Strength ISO 179 KJ/m2 6 10 9 6 4 7 7 13 8 5 3 3
Charpy Impact Strength ISO 179 KJ/m2
Rockwell Hardness(R scale) ISO 2039
Rockwell Hardness(M scale) ISO 2039
Linear Expansion Coefficient ISO 11359 ×10
-5
㎜/㎜/℃ 10 10 10 10 10 10 10 10 10 10 10 8
Deflection Temperature Under
Load (1.82MPa)
ISO 75 ℃ 100 90 90 92 100 100 95 90 85 100 100 110
Deflection Temperature Under
Load (0.45MPa)
ISO 75 ℃ 165 155 155 161 164 165 160 154 152 157 157 160
UL-94(1/16 in) UL-94 Rank 1.6mm - 1.5mmt HB 1.5mmt HB 1.5mmt HB 1.5mmt HB - - - - - - UL-94(1/32 in) UL-94 Rank 0.8mm
0.70mmt
HB
0.75mmt
HB
0.75mmt
HB
-
0.75mmt
HB
0.70mmt
HB
0.70mmt
HB
0.75mmt
HB
-
0.75mmt
HB
0.75mmt
HB
0.71mmt HB
UL94-5VA UL94-5VA mm - - - - - - - - - - - -
Tracking Resistance IEC 60112 3mm - - - - - - - - - - - Dielectric Strength IEC 60243 KV/㎜ - - - - - - - - - - - Surface Resistivity IEC 60093 Ω 23℃50%RH - - - - - - - - - - - Volume Resistivity IEC 60093 Ω・㎝ 23℃50%RH - - - - - - - - - - - Dielectric Loss Tangent IEC 600250 100HZ - - - - - - - - - - - Dielectric Loss Tangent IEC 600250 1MHZ - - - - - - - - - - - Permittivity IEC 600250 100HZ - - - - - - - - - - - Permittivity IEC 600250 1MHZ - - - - - - - - - - - Asahi Kasei % 1.8~2.2 1.8~2.2 1.8~2.2 1.8~2.2 1.8~2.2 1.8~2.2 1.8~2.2 1.8~2.2 1.6~2.0 1.6~2.0 1.6~2.0 1.4~1.6
ISO 294-4 %
Refractive Index ISO 489
Transmission ISO13468-1
Melt Flow Rate ISO 1133 g/10min 34 12 25 25 9 17 22 2.5 3 9 30 25P
h ys ic a ls The date provided for these properties are typical values,intended only as guides,and should not be construed as sales specifications.
For any intended use that may involve food contact,therefore,please consult with Asahi Kasei Chemicals Corporation.
For safety in the handling and use of TenacTM,TenacTM-C,please refer to the relevant Material Safety Data Sheet issued by Asahi Kasei Chemicals Corporation.
M
e c h an ic al T
h e rm al F
la m m a bi lit
y E
le c tr ic al s Mold shrinkage (Flow / Right-angle)
Mold shrinkage (Flow / Right-angle)
TENAC
TM
-C
Test method Units Condition TFC64 TFC84 TFC77 EF750 EF850
Density ISO 1183 g/cm3 1.37 1.38 1.41 1.41 1.41
Moisture Regain ISO 62 %
Yield Stress ISO 527 MPa 23℃50%RH 35
Tensile Strain at Yield ISO 527 % 23℃50%RH
Tensile Stress at Break ISO 527 MPa 23℃50%RH 35 38 52 50
Tensile Strain at Break ISO 527 % 23℃50%RH 2 31 3 10 5
Tensil Modulus ISO 527 MPa 23℃50%RH 2200 2700 3200 2600 3300
Flexural strenght ISO 178 MPa 23℃50%RH
Flexural Modulus ISO 178 MPa 23℃50%RH 2100 2600 3100 2500 3200
Notched Charpy Impact Strength ISO 179 KJ/m2 1.5 3 2 3 2
Charpy Impact Strength ISO 179 KJ/m2
Rockwell Hardness(R scale) ISO 2039
Rockwell Hardness(M scale) ISO 2039
Linear Expansion Coefficient ISO 11359 ×10-5㎜/㎜/℃ 6
Deflection Temperature Under Load
(1.82MPa)
ISO 75 ℃ 85 83 85 100 95
Deflection Temperature Under Load
(0.45MPa)
ISO 75 ℃ 146 145 145 162 153
UL-94(1/16in) UL-94 Rank 1.6mm - - - 1.5mmt HB UL-94(1/32in) UL-94 Rank 0.8mm 0.75mmt HB 0.75mmt HB 0.75mmt HB 0.75mmt HB 0.75mmt HB
UL94-5VA UL94-5VA mm - - - - -
Tracking Resistance IEC 60112 3mm - - - - Dielectric Strength IEC 60243 KV/㎜ - - - - Surface Resistivity IEC 60093 Ω 23℃50%RH 100~101 100~101 100~101 101~102 101~102
Volume Resistivity IEC 60093 Ω・㎝ 23℃50%RH 100~101 100~101 100~101 101~102 101~102
Dielectric Loss Tangent IEC 600250 100HZ - - - - Dielectric Loss Tangent IEC 600250 1MHZ - - - - Permittivity IEC 600250 100HZ - - - - Permittivity IEC 600250 1MHZ - - - - Asahi Kasei % 1.3~1.6 1.2~1.6 1.2~1.6 1.6~2.0 1.4~1.8
ISO 294-4 %
Refractive Index ISO 489
Transmission ISO13468-1
Melt Flow Rate ISO 1133 g/10min - 1 1 10 18
Mold shrinkage (Flow / Right-angle)
P
h ys ic al s The date provided for these properties are typical values,intended only as guides,and should not be construed as sales specifications.
For any intended use that may involve food contact,therefore,please consult with Asahi Kasei Chemicals Corporation.
For safety in the handling and use of TenacTM,TenacTM-C,please refer to the relevant Material Safety Data Sheet issued by Asahi Kasei
Chemicals Corporation.
Electro Conductive
M
e c h an ic al T
h e rm al F
la m m ab i lit
y E
le c tr ic al s Mold shrinkage (Flow / Right-angle)

PDF Document reader online

This website is focused on providing document in readable format, online without need to install any type of software on your computer. If you are using thin client, or are not allowed to install document reader of particular type, this application may come in hand for you. Simply upload your document, and Docureader.top will transform it into readable format in a few seconds. Why choose Docureader.top?

  1. Unlimited sharing - you can upload document of any size. If we are able to convert it into readable format, you have it here - saved for later or immediate reading
  2. Cross-platform - no compromised when reading your document. We support most of modern browers without the need of installing any of external plugins. If your device can oper a browser - then you can read any document on it
  3. Simple uploading - no need to register. Just enter your email, title of document and select the file, we do the rest. Once the document is ready for you, you will receive automatic email from us.